Synthetic rubber

ProductAppearanceProperties and applicationsChlorine content
(%)
Sulphur content
(%)
Mooney
ML (1+4)
@ 100°C
CSM 20off-white irregular chipsvery good resistance to ozone, weathering, oil and chemicals
Good low-temperature flexibility;
rubber cements, adhesives, tapes, coatings
27 – 311.3 – 1.723 – 33
CSM 30off-white irregular chipsCSM grade with highest chlorine content; predestined for oil contact and flame retardant applications: anti-corrosion coattings, wires and cables, tubes, membranes41 – 450.8 – 1.235 – 45
CSM 40 (3304)off-white irregular chipslow-viscosity type of standard grade CSM 40; pls. see below33 – 370.8 – 1.240 – 49
CSM 40 (3305)off-white irregular chipsgeneral purpose grade CSM 40, good all-round properties reg. resistance to ozone, weathering, oil and chemicals; tubes, oil-seals, roll coverings, modification of other elastomers33 – 370.8 – 1.250 – 60
CSM 45off-white irregular chipsgood abrasion resistance, very good weathering and heat resistance, moderate oil resistance; roofings, floorings, magnetic rubber parts, radiation shieldings22 – 250.8 – 1.232 – 42
CSM 4085off-white irregular chipshigh–mw CSM-Type 4085 suited for highly filled compounds; tubes, automotive hoses, seals / articles in contact with oil, cable sheathings, roll coverings34 – 380.8 – 1.285 – 95
luvomaxx®-csm-chlorosulphonated-polyethylene.pdf
ProductAppearanceProperties and applicationsVolatile matter
(%)
TGMooney
ML (1+4)
@ 100°C
LUVOMAXX 3,4 PolyisopreneBales 
  • very good mechanical damping/ sound damping properties
  • improved grip and wet grip
  • straightforward co-vulcanization in blends with NR and SBR. Car and truck tyres, soles for climbing, walking and safety boots, sailing shoes, golfing items, car sports seats, insulation materials for cars, machinery as well as household and office appliances
 
< 0.5- 10 °C65 – 75
poly-3,4-isoprene-rubber.pdf

Examples shown; further special grades on request


Injection moulding grades

ProductAppearanceDensity (g/cm3)Tensile strength
(MPa)
Elong. at break
(%)
Shore hardn.
10s,23°C
Tear str.
(kN/m)
Comp. set
22h@70°C
(%)
TPV 10-45A
black granules0.954.245045 (A)2038
TPV 10-80Ablack granules0.977.545083 (A)4240
TPV 11-73A
black granules0.967.540074 (A)3635
TPV 11-80A
black granules0.9611.155082 (A)4033
TPV 11-50D
black granules0.932470050 (D)113n.a.
ASTM
D-792
ASTM
D-412
ASTM
D-412
ASTM
D-2240
ASTM
D-624
ASTM
D-395
injection-moulding-grades.pdf

Sealing and profile grades

ProductAppearanceDensity
(g/cm3)
Tensile strength
(MPa)
Elong. at break
(%)
Shore hardn.
10s,23°C
Tear str.
(kN/m)
Comp. set
22h@70°C
(%)
TPV 14-50A
black granules0.934.560055 (A)2525
TPV 10-60A
black granules0.975.340063 (A)2728
TPV T18-75A
black granules0.908.160075 (A)4645
ASTM
D-792
ASTM
D-412
ASTM
D-412
ASTM
D-2240
ASTM
D-624
ASTM
D-395
sealing-and-profile-grades.pdf

Wire and cable grades

ProductAppearanceDensity
(g/cm3)
Tensile Strength
(MPa)
Elong. at Break
(%)
Shore hardn.
10s,23°C
Tear str.
(kN/m)
Comp. set
22h@70°C
(%)
TPV H721-70A
black granules0.977.555070 (A)4030
TPV 12-80A
black granules1.217.345083 (A)4245
TPV 721-93A
black granules0.961360093 (A)6550
ASTM
D-792
ASTM
D-412
ASTM
D-412
ASTM
D-2240
ASTM
D-624
ASTM
D-395
wire-and-cable-grades.pdf

Automotive ventilation pipes, dust caps

ProductAppearanceDensity
(g/cm3)
Tensile strength
(MPa)
Elong. at break
(%)
Shore hardn.
10s,23°C
Tear str.
(kN/m)
Comp. set
22h@70°C
(%)
TPV H721-70A
black granules0.936.360054 (A)2929
TPV 12-80A
black granules0.9513.762290 (A)9346
TPV 721-93A
black granules0.9522.383048 (D)13860
ASTM
D-792
ASTM
D-412
ASTM
D-412
ASTM
D-2240
ASTM
D-624
ASTM
D-395
automotive-ventilation-pipes,-dust-caps.pdf

Deformation joints, shims, spacers

ProductAppearanceDensity
(g/cm3)
Tensile strength
(MPa)
Elong. at break
(%)
Shore hardn.
10s,23°C
Tear str.
(kN/m)
Comp. set
22h@70°C
(%)
TPV 11-64A
black granules0.976.655464 (A)2221
TPV 810-80A
black granules0.9710.257883 (A)5338
TPV 814-40D
black granules0.9713.568441 (D)10930
ASTM
D-792
ASTM
D-412
ASTM
D-412
ASTM
D-2240
ASTM
D-624
ASTM
D-395
deformation-joints,-shims,-spacers.pdf

Automotive parts, moulded goods

ProductAppearanceDensity
(g/cm3)
Tensile strength
(MPa)
Elong. at break
(%)
Shore hardn.
10s,23°C
Tear str.
(kN/m)
Applications
TPV 830-62A
black granules0.935.545058 (A)25covers
TPV 10-35D
black granules0.9515.163436 (D)91side airbags
TPV 14-40D
black granules0.941558042 (D)96hub caps
ASTM
D-792
ASTM
D-412
ASTM
D-412
ASTM
D-2240
ASTM
D-624
automotive-parts,-moulded-goods.pdf